Cation distribution correlated with magnetic properties of nanocrystalline gadolinium substituted nickel ferrite

Abstract

Nano crystalline NiFe2-xGdxO4 (0.0 <= x <= 0.4) ferrite was prepared by citrate method. The samples were characterized with X-ray diffraction, FT-IR spectroscopy, TEM and magnetic measurements. The effect of Gd3+ cations substitution on structural, microstructural and magnetic properties of prepared nanoparticles was investigated. From Rietveld analysis, the system was found to be inverse spinel structure with Gd3+ residing on octahedral B-site 16c and the grain boundary, while Ni2+ occupying the B-site at both 16c and 16d. The lattice parameter (a) changes nonmonotonically, first increases then decreases with Gd doping content. The M-H and M-T relations had demonstrated a change in the magnetic moment and a ferrimagnetic-superparamagnetic transition in the ferrite system For low temperature measurements, an increase in gadolinium content resulted in increasing the coercive field while the saturation of magnetization (M-s), first deceases then increases with Gd doping content. At room temperature M-s decreases with increasing Gd substitution. (C) 2015 Elsevier B.V. All rights reserved.