Fracture properties of asphalt mixtures containing high content of reclaimed asphalt pavement (RAP) and eco-friendly PET additive at low temperature

Abstract

Low-temperature cracking is one of the main types of distress that affects asphalt pavement performance over its service life. At the same time, the accumulation of plastics, especially polyethylene terephthalate (PET), and the potentially harmful effects of these plastics requires special attention in order to find ways to reduce them. Previous studies have paid less attention to the impact of PET on low-temperature cracking in asphalt mixtures and the simultaneous interaction between PET and reclaimed asphalt pavement materials (RAP) on fracture behavior of asphalt mixture. In this study, a value-added substance called PET Additive (PA), which is extracted from chemical processing of PET was blended with asphalt binder at different dosages (1-3 %) to use in the mixture of hot mix asphalt (HMA). Reclaimed Asphalt Pavement (RAP) was also added to the HMA mixtures at rates of 25 and 50 % by aggregate mass and the resulting asphalt mixtures were tested to characterize the load carrying ability and cracking resistance indexes of the modified HMA mixtures. Circular shaped test specimens with different mixture types and different geometries were manufactured. Results showed that the asphalt mixture containing PA has better performance than the control mixture; among all mixture types, a mixture containing 2 % PA and 25 % RAP had the better fracture resistance at low temperatures. Finally, the results demonstrate that the fracture behavior in Edge Notch Disc Bend (ENDB) and Semi-Circular Bend (SCB) specimens had similar trends.