Synthesis and characterization of CuFe2O4 nanorods synthesized by polyol route

Abstract

Uniform, high quality, CuFe2O4 nanorods with high aspect ratios were synthesized by a surfactant-free single step polyol process at 220 degrees C. The structure of the product was characterized by XRD and FT-IR, and the morphology of the product was analyzed by SEM. The results showed that the as-prepared nanorods have a uniform cross-section and with average diameter of similar to 100 nm and aspect ratio in the range of 13-52. X-ray line profile fitting resulted in crystallite size of 15 nm, which reveals the polycrystalline nature of these nanorods. Magnetic characterization of product was performed by EPR and VSM techniques and the results show that the CuFe2O4 nanorods are ferromagnetic. The line width of the resonance lines in FMR is about 1.8 kOe which may originate from different resonance fields of randomly distributed nanocrystals which have different orientation of magnetic easy axes. (C) 2009 Elsevier B.V. All rights reserved.