The effect of additive manufacturing on the initial High temperature oxidation properties of RE-containing FeCrAl alloys

Abstract

The effect of additive manufacturing on the high temperature oxidation properties of FeCrAl materials was investigated. For this purpose, additively manufactured Kanthal AM100 cut parallel and perpendicular to the building direction and hot-rolled Kanthal AF as a reference were exposed to air at 900 and 1100 degrees C for 168 h. AM100 performed slightly better than AF in terms of mass gain. Nevertheless, an oxide scale with local differences in thickness formed on AM100 due to the bimodal grain structure of the underlying metal, which was composed of coarse-grained cuboidal repeating units (100 mu m wide), separated by fine-grained rims.