dc.contributor.authorKazan, S.
dc.contributor.authorMikailzade, F. A.
dc.contributor.authorOzdemir, M.
dc.contributor.authorAktas, B.
dc.contributor.authorRameev, B.
dc.contributor.authorIntepe, A.
dc.contributor.authorGupta, A.
dc.date.accessioned2025-10-29T11:19:30Z
dc.date.issued2010
dc.departmentFakülteler, Temel Bilimler Fakültesi, Fizik Bölümü
dc.description.abstractFerromagnetic resonance (FMR) studies of epitaxial La2NiMnO6 (LNMO) thin films on (100) oriented SrTiO3 and (110) oriented NdGaO3 substrates at room temperature are presented. Observation of FMR spectra above the Curie temperature of this compound confirms the presence of magnetic ordering in LNMO thin films at room temperature. Best fitting of FMR spectra has been made on the assumption of the coexistence of two magnetic phases with different easy and hard axis periodicities in the film plane of LNMO. The spectra of the films on various substrates are characterized by different in-plane and out-of-plane symmetries, which indicates the existence of different epitaxial growth on the substrates with different crystal symmetries and orientations. (C) 2010 American Institute of Physics. [doi:10.1063/1.3481678]
dc.description.sponsorshipState Planning Organization of Turkey [2009K120730]
dc.description.sponsorshipResearch Projects Commission of Gebze Institute of Technology [2009-A11]
dc.description.sponsorshipThis work was supported by State Planning Organization of Turkey through the Project No. 2009K120730. F.M. is indebted to Research Projects Commission of Gebze Institute of Technology for supporting this work by the Grant No. 2009-A11.
dc.identifier.doi10.1063/1.3481678
dc.identifier.issn0003-6951
dc.identifier.issn1077-3118
dc.identifier.issue7
dc.identifier.orcid0000-0002-8183-5733
dc.identifier.orcid0000-0003-0828-8312
dc.identifier.orcid0000-0002-1785-7209
dc.identifier.scopus2-s2.0-77956014987
dc.identifier.scopusqualityQ1
dc.identifier.urihttps://doi.org/10.1063/1.3481678
dc.identifier.urihttps://hdl.handle.net/20.500.14854/8181
dc.identifier.volume97
dc.identifier.wosWOS:000281153600057
dc.identifier.wosqualityQ1
dc.indekslendigikaynakWeb of Science
dc.indekslendigikaynakScopus
dc.language.isoen
dc.publisherAmer Inst Physics
dc.relation.ispartofApplied Physics Letters
dc.relation.publicationcategoryMakale - Uluslararası Hakemli Dergi - Kurum Öğretim Elemanı
dc.rightsinfo:eu-repo/semantics/openAccess
dc.snmzKA_WOS_20251020
dc.subjectcrystal orientation
dc.subjectcrystal symmetry
dc.subjectCurie temperature
dc.subjectepitaxial layers
dc.subjectferromagnetic resonance
dc.subjectlanthanum compounds
dc.subjectneodymium compounds
dc.subjectnickel compounds
dc.subjectstrontium compounds
dc.titleFerromagnetic resonance in double perovskite epitaxial thin films of La2NiMnO6 on SrTiO3 and NdGaO3 substrates
dc.typeArticle

Dosyalar

Koleksiyon

WoS İndeksli Yayınlar Koleksiyonu
Scopus İndeksli Yayınlar Koleksiyonu
Temel Bilimler Fakültesi Koleksiyonu