Enhancing linezolid activity in the treatment of oral biofilms using novel chitosan microneedles with iontophoretic control

Abstract

This study aimed to prepare and assess active microneedle (MN) patches based on a novel biomaterial and their effective coupled (physical and electrical) transdermal delivery of a model drug (Linezoid). Modified MN patches (e.g. fabricated from Linezoid, boronated chitosan, polyvinyl alcohol and D-sorbitol) were engineered using a vacuum micromoulding method. Physicochemical, FTIR (Fourier transform infrared), in-silico, structural and thermal analysis of prepared formulations were conducted to ascertain MN quality, composition and integrity. In-vitro mechanical tests, membrane toxicity, drug release, antibiofilm, ex-vivo mucoadhesion, insertion and invivo antibiofilm studies were performed to further validate viability of the coupled system. Optimized MN patch formulation (CSHP3 - comprising of 3 % w/v boronated chitosan, 3.5 % w/v PVA and 10 % w/w D-sorbitol) exhibited sharp-tipped, equi-distant and uniform-surfaced micron-scaled projections with conforming physicochemical features. FTIR analysis confirmed modification (i.e., boronation) of chitosan and compatibility as well as interaction between CSHP3 constituents. In-silico analysis indicated non-covalent interactions between all formulation constituents. Moreover, boronated chitosan-mucin glycoprotein complex showed a stronger bonding ( 1.86 times higher CScore) as compared to linezolid-mucin counterpart. Thermal analysis indicated amorphous nature of CSHP3. A 1.42 times higher tensile strength was displayed by CSHP3 as compared to control (i.e., pure chitosan, polyvinyl alcohol and D-sorbitol-based MN patch). Membrane toxicity study indicated non-toxic and physiological compatible nature of CSHP3. Within 90 min, 91.99 +/- 2.3 % linezolid was released from CSHP3. During release study on agarose gel, CSHP3-iontophoresis treatment resulted in a 1.78 and 1.20 times higher methylene blue-covered area and optical density, respectively, within 60 min as compared to CSHP3 treatment alone. Staphylococcus aureus biofilms treated with CSHP3 exhibited 65 +/- 4.2 % reduction in their mass. CSHP3 MN patches remained adhered to the rabbit oral mucosa for 6 +/- 0.15 h. Mucosa treated with CSHP3 and CSHP3-iontophoresis combination showed a generation of pathways in the epithelium layers without any damage to the underlying lamina propria. Eradication of Staphylococcus aureus from oral mucosal wounds and complete tissue regeneration was recorded following 7-day treatment using CSHP3-iontophoresis coupled approach.