Effect of Fe Concentration on the High Temperature Oxidation Behavior of Fex(CrAlNi)100-x Medium Entropy Alloys

Abstract

In this study, effect of Fe concentration on the high temperature oxidation and microstructural stability of Fex(CrAlNi)(100-x) alloys (x = 25, 35, 45, 55, 65) at 1100 C-degrees up to 168 h was investigated in air. Increasing Fe concentration decreased the molar fraction of B2 phase in as-cast alloys. However, microhardness values experienced only a 10% reduction (Fe-25: 517.7 +/- 19 HV, Fe-65: 470.6 +/- 22 HV) due to well-distributed B2 precipitates. After the exposures, coarsening of B2 precipitates was observed in all alloys, leading to a microhardness reduction of 20-25% after 168 h. Single-phase alpha-Al2O3 scales were formed on Fe-25-Fe-55 alloys. However, increasing Fe concentration resulted in deeper depletion zones due to reduced molar fraction and Al concentration of B2 phase. Moreover, Fe-65 alloy failed to develop a protective alpha-Al(2)O(3 )scale due to decreased molar phase fraction and Al concentration of B2 precipitates, along with the low Cr concentration of the A2 phase. Additionally, alpha-Al2O3 scales were highly wrinkled due to the absence of reactive elements. Absence of reactive elements also resulted in oxide spallation and seemed to intensify with the increasing Fe concentration. Possible reasons for the increased oxide spallation with the increasing Fe concentration are discussed. Nevertheless, Fe-25-Fe(55 )alloys displayed oxidation properties comparable to those of lean FeCrAl alloys while also possessing enhanced mechanical properties due to B2 reinforcement.